1. Die casting taabolo kɔlɔsi kosɛbɛ .
The temperature of the aluminum water in the holding furnace should be controlled at ±3℃in order to stabilize the stirring temperature. The temperature after stirring must be adjusted according to the chemical composition of each furnace to ensure that the solid phase rate is stable at ±2%. The temperature of the mold must be checked and controlled so that the alloy can be smoothly filled and ordered to solidify. It is necessary to rationally formulate and adjust the process Die casting masin paramɛtiriw bɛ kɛ waati bɛnnen na, ani ka die castings lajɛ walasa ka die castings ka jogo jira.
2, a bɛ se ka kɛ ko a bɛ se ka kɛ ka furaji fiyɛli baara kɛ .
Pay attention to how much the release agent coating is applied, avoid too much coating, too little or miss the coating. The parts where the castings are difficult to demold can be sprayed with more paint, and the parts that are easily released from the mold are less sprayed. When spraying the paint, use a spray gun to move from top to bottom, so that the water accumulated in the cavity flows from top to bottom, and the excess water is blown out of the Cavity. cavity bɛ nɔrɔ nɔgɔya la nɔgɔ yɔrɔ la, wa a siɲɛ fɔlɔ bɛ fiyɛ ka nɛnɛ, o kɔfɛ a fiyɛlen don ka kɛ finimugu ye min bɛ kɛ ka finimugu da. Aw kana gɛrɛ kojugu furaji la walasa ka jaji bali ka woyo ka bɔ a kɔnɔ. fiyɛli kɔfɛ, ka fiɲɛ kɛ ka a fiyɛ ka tɛmɛ ani ka a lajɛ ni a bɛ se ka kɛ sababu ye ka a ka ca ni a ye, a ka kan ka a ka so kɔnɔ walima ka a kɛ ka a kɛ ka a kɛ ka a kɛ ka a kɛ ka a kɛ ka a kɛ ka a kɛ ka a ka so. Aw bɛ fiɲɛ bila walasa ka ji bali ka kɛ gazi caman ye funteni kɔfɛ, fo a ka fɛnɲɛnamafagalan bɛ ni pores. ye, a bɛ kɛ ni casting under-casting ye, a bɛ nɛnɛ, foaming, min jɔyɔrɔ ka bon kosɛbɛ pores sɔrɔli la ka bɔ castings kɔnɔ.
3. Aw ye aw yɛrɛ tanga ni aw bɛ baara kɛ ni filimu funteni ye die casting machine kɔnɔ .
Mold temperature machine ka mold hot moule bɛ baara kɛ, ni moule funteni daminɛna, liquide alloy bɛ se ka kɛ ka moule hot moule 5-10 mold kɛ ni teliya dɔgɔman ye, ani o kɔfɛ normal semi-solide alloy ani semi-solid die casting paramètres bɛ kɛ ka die casting production, walasa moule ka se ka lakana{{